Index > Products > Alloy Mica Series > A5230

Alloy Mica SEM micrograph

Zero α® Alloy Mica

A5230



Introduction

Alloy-Mica Zero α® is a kind of inorganic material, which in appearance of flake under microscope, with the feature of high aspect ratio and low hardness. For different organic compatibility, the surface of flakes is treated with various silane as coupling agent; then special features of this product is able to be compatible to aromatic polymers, ex. Nylon6, Nylon 66, Nylon HTN, Nylon 46, PPO…etc.


★ To improve the performance of dispersion in compound system.
★To enhance the properties such as: HDT, flame retardant, heat conductivity, anti-yellow aging weathering, and increase flexural strength…etc.


Properties

The typical properties of the original Alloy Mica are listed as follows:

Chemical Composition of Mica ± 5%)
SiO2
53.5%
Al2O3
33.4%
K2O
5.6%
CaO
0.3%
MgO
0.4%
Fe2O3
0.98%
Na2O
0.3%
I g Loss
5.0%

Physical Properties
Moisture content
1.2 wt% max
Specific gravity
2.76
Oil absorption
40 ~ 60
pH value
7.0 ± 1.5
Brightness
65 ± 2
Refractive index
1.594 ~ 1.616
Particle size
Below45μm>99%
Average particle size(D50)
15μm
Hardness
2.20 ~ 2.50

General Compound Recommendation:
Halogen free
PE/PP/POE 50% 50%
phosphorus/nitrogen 20~25% 10~12%
Alloy mica A5230   15% (no less than12%)
Glass fiber 15% 13%
UL94 (1/8”) V0 V0

Halogen free without glass fiber
PE/PP/TPO 50~60%
phosphorus/nitrogen 10%
Alloy mica A5230 20~35%
UL94 (1/8”) V0

Packing and Storage

Standard package: 25 kgs of Alloy Mica powders packed in PE laminated Kraft paper bag.

Shelf life is up to 180 days if stored in cool and low humidity environment.


Remarks

Compounding Application:

  1. 1.When using A5230 as filling powder, a twin-screw extruder, which equipped with a side-feeding system in front of extruder, should be applied.
  2. - A5230 powder feed in system via side-feeding system;
  3. - If there is no side-feeding system in the front of extruder, two separated feeders should be prepared that one for resin while A5230 filling powder, the other.

  4. 2. In order to avoid the return flow of fed resin, the upstream temperature of extruder should be 5~10℃ higher than downstream.
  5. 3. A5230 filling powder should be fed in system after the plastic feeding process is stable.
  6. 4. The recommend dosage of A5230 is 12 wt%~35 wt% of composite plastic.